Search results for " Anodic Alumina Membrane"
showing 10 items of 21 documents
Influence Of The Electrical Parameters On The Fabrication Of Copper Nanowires Into Anodic Alumina Templates
2009
Abstract Metallic copper nanowires have been grown into the pores of alumina membranes by electrodeposition from an aqueous solution containing CuSO 4 . and H 3 BO 3 at pH 3. In order to study the influence of the electrical parameters on growth and structure of nanowires, different deposition potentials (both in the region where hydrogen evolution reaction is allowed or not) and voltage perturbation modes (constant potential or unipolar pulsed depositions) were applied. In all cases, pure polycrystalline Cu nanowires were fabricated into template pores, having lengths increasing with the total deposition time. These nanowires were self-standing, because they retain their vertical orientati…
Sintesi per via elettrochimica di nanowires di leghe Co-Sn
2008
Fabrication and Photoelectrochemical Behavior of Ordered CIGS Nanowire Arrays for Application in Solar Cells
2010
In this work, we report some preliminary results concerning the fabrication of quaternary copper, indium, gallium, and selenium CIGS nanowires that were grown inside the channels of an anodic alumina membrane by one-step potentiostatic deposition at different applied potentials and room temperature. A tunable nanowire composition was achieved through a manipulation of the applied potential and electrolyte composition. X-ray diffraction analysis showed that nanowires, whose chemical composition was determined by energy-dispersive spectroscopy analysis, were amorphous. A composition of Cu0.203In0.153Ga0.131Se0.513, very close to the stoichiometric value, was obtained. These nanostructures wer…
Electrodeposition of CeO2 and Co-Doped CeO2 Nanotubes by Cyclic Anodization in Porous Alumina Membranes
2013
An anodic electrodeposition process is proposed to prepare CeO2 and Co-doped CeO2 nanotubes. Anodic alumina membrane is used as template and linear sweep voltammetry is employed to allow the formation of nanotubes without alumina dissolution. SEM micrographs showed large arrays of well defined and aligned NTs, which resulted to be crystalline soon after deposition according to XRD diffraction patterns and Raman Spectroscopy.
Lead Nanowires for Microaccumulators Obtained Through Indirect Electrochemical Template Deposition
2010
Metallic lead nanowires were deposited within pores of commercial anodic alumina membranes having an average pore diameter of 210 nm. "Direct" electrodeposition was attempted from 0.1 M Pb(NO 3 ) 2 aqueous solution with a variable concentration of H 3 BO 3 as a chelating agent, but it gave unsatisfactory results. An "indirect" two-step deposition procedure was then adopted, consisting of the anodic electrodeposition of α-PbO 2 nanowires, followed by their in situ reduction to metallic lead. Both these processes occurred at a high rate so that the indirect method led to a complete template pore filling with pure polycrystalline Pb in short times and with a high current efficiency.
Template electrosynthesis of La(OH)3 and Nd(OH)3 nanowires using porous anodic alumina membranes
2007
High quality arrays of Ln(OH)3 (Ln = La, Nd) nanowires have been successfully fabricated for the first time by an electrochemical process using anodic alumina membrane templates. A physico-chemical characterisation of electrodeposited hydroxides has been carried out by different techniques (XRD, SEM and EDX). The results show that the synthesized nanostructures are crystalline, dense, continuous, well aligned, and with high aspect ratio, suggesting further development of possible applications in the lanthanide family species. Keywords: Nanowires, Anodic alumina membranes, Hydroxide electrodeposition, Template, Lanthanide compounds
Comments on 'formation and characterization of nanotubes of La(OH) 3 obtained using porous alumina membranes'
2010
New experimental evidence concerning the formation of La(OH)3 nanowires on anodic alumina membranes by cathodic polarization in 0.05 M lanthanum nitrate solution is provided to further support the conclusions previously reached in our work (Bocchetta et al 2007 Electrochem. Commun. 9 683-8) and recently criticized by González-Rovira et al (Nanotechnology 2008 19 495305). Some unconvincing aspects of the paper of González-Rovira et al, according to which the same electrochemical process should lead to the formation of hydroxycarbonate nanotubes, are also discussed.
Growth and Characterization of Ordered PbO[sub 2] Nanowire Arrays
2008
Large arrays of PbO 2 nanowires having high aspect ratios (length-to-width ratio) were grown by potentiostatic electrodeposition into anodic alumina templates under anodic polarization. Different electrolytic solutions were used in order to obtain nanowires of pure α-PbO 2 , pure β-PbO 2 , and a a + β mixture, We have found that, in a lead nitrate bath, a crystallographic structure of nanowires depends on pH; this latter was varied adding diluted nitric acid to the electrolyte. Nanowires of pure β-PbO 2 were obtained at pH 0.6, while mixed α-PbO 2 + β-PbΟ 2 nanowires were grown at pH 2. Pure α-phase was obtained in a bath containing lead acetate at pH 6.6. In all deposition conditions, nano…
Characterization of Sn-Co nanowires grown into alumina template
2009
Nanowires of Sn-Co alloys were grown inside the channels of anodic alumina membrane by potentiostatic deposition. The scanning electron microscope images showed the formation of cylindrical nanowires whose height was increasing with deposition time. The X-ray patterns did not show significant diffraction peaks, suggesting the formation of amorphous phases. The higher content of Co in the nanowires, in comparison to the initial composition of the electrolytic bath, was attributed to a higher rate of Co electrodeposition. These nanowires seem to possess specific features suitable for innovative application in the field of Li-ion batteries due to their dimensional stability and high specific s…